FR4 Copper Clad Laminate sheet
Newlytrend Copper Clad Laminate FR4 (single or double sided)is a kind of copper foil covered laminated board formed through heat pressing after the electric industry alkali-free glass fiber dips into thermoset epoxy resins and is covered with copper foil at one side or both sides. Usually used in PCB with printed circuit on one or both sides of computers, home electric appliances and other lines.
A. The details of our fr4 copper clad laminate sheet
General Data |
Core Layer Color |
white,yellow,black |
Sheets Thickness(mm) |
0.2mm-4mm |
|
Copper thickness |
18 μm(1/2 oz),35μm(1 oz),or customized |
|
Stock Size (inch) |
41''X49'', 43"X49", other sizes can be customized |
|
Package |
1. Wooden pallet with carton. |
|
2. Plastic pallet with carton. |
||
3. Wooden wooden pallet with wooden case. |
||
4. According to customer requirements. |
||
Sample |
1.sample time: wthin 3-7 days |
|
2.Sample charge:According to product details |
||
3.Send sample:Via DHL, TNT, UPS, Fedex |
||
4.Small size sample can be free given if you need it for testing the quality |
||
Payment |
TT or Western Union |
|
Delivery Time |
7-15 days according to the order quantity |
|
Shipping Port |
Shenzhen |
B. Data sheet:
Item |
Test condition |
Unit |
SPEC |
Typical Value |
|
Tg |
DSC |
°C |
≥170 |
175.2
|
|
Peel strength(1OZ) |
288°C,10S |
N/mm |
≥1.05 |
1.41 |
|
Thermal Stress |
288°C,10S/solder dip |
____ |
No delamination |
180S/ No delamination
|
|
Flammability |
N/mm2 |
LW |
≥415 |
580 |
|
CW |
≥345 |
482 |
|||
Surface Resistivity |
After moisture |
MΩ |
≥1. 0×104 |
2,52×107 |
|
Volume Resistivity |
After moisture |
MΩ.cm |
≥1.0×105 |
3.21×108 |
|
Dielectric Constant |
1MHz C-24/23/50 |
____ |
≤5.4 |
4.7 |
|
Loss Tangent |
1MHz C-24/23/50 |
____ |
≤0.035 |
0.016 |
|
Arc Resistivity |
D-48/50+D-0.5/23 |
S |
≥60 |
122 |
|
Dielectric Breakdown |
D-48/50+D-0.5/23 |
KV |
≥40 |
58 |
|
Moisture Absorption |
D-24/23 |
% |
≤0.5 |
0.1 |
|
Td |
Weight loss 5% |
°C |
340 |
347 |
|
CTE Z—axis |
Alpha 1 |
TMA |
ppm/°C |
≤60 |
45 |
Alpha 2 |
ppm/°C |
≤300 |
270 |
||
50-260°C |
% |
≤3.0 |
2.9 |
||
T288
|
TMA |
min |
≥15 |
30 |
|
CTI |
IEC60112 Method |
V |
175~250(Grade 3) |
200 |
C. The inspection of fr4 copper clad laminate sheet
1.The end face of foil covered board should be tidy without any delamination and crackle .
2. Any bubble, wrinkle, pin hole, deep nick, pitting and glue spot on the copper foil covered face is not allowed. Any color changing or dirty can be easily removed by density 1.02g/cm3 hydrochloric acid or proper organic solution.
3.On laminated face, the defects such as bubble, impressed pitting, nick and glue lack and outer impurity which retard its use are not allowed .
D. Suggestion for use
Please baking the laminate at 150°C,2 hours before using.
Please pay attention to the machining for the interbedded energy is lower than the normal FR-4.Rilling parameters are mainly dependent on hole size ,layer thickness, layer number ,copper thickness and stack height.
The following drilling parameters are for reference only .Typical drilling parameters for 0.4 ~1.0mm drills are as follows:
speed :45 ~105 KRPM
Feed rate:50~150 IPM
Retract rate:;500~1000 IPM
Suggest hit count:1500 HITS
Stack height:≤2pnls(2~6 layers), 1pnls(≤8 layers)